PbS QD
Grade: PL emission :1550±50 nm
Concentration: 50mg
FWHM:120-150 nm
PbS QD
Grade: PL emission :1450±50 nm
Concentration: 50mg
FWHM:120-150 nm
PbS QD
Grade: PL emission :1350±50 nm
Concentration: 50mg
FWHM:120-150 nm
PbS QD
Grade: PL emission :1250±50 nm
Concentration: 50mg
FWHM:120-150 nm
PbS QD
Grade: PL emission :1150±50 nm
Concentration: 50mg
FWHM:120-150 nm
PbS QD
Grade: PL emission :1050±50 nm
Concentration: 50mg
FWHM:120-150 nm
PbS QD
Grade: PL emission :950±50 nm
Concentration: 50mg
FWHM:120-150 nm
PbS QD
Grade: PL emission :850±50 nm
Concentration: 50mg
FWHM:120-150 nm
CdSe/ZnS QD
Grade: PL emission :645±10 nm
Concentration: 20 nmole QD / mL
Surface Group :MPA-COOH
FWHM≤ 30 nm
CdSe/ZnS QD
Grade: PL emission :625±10 nm
Concentration: 20 nmole QD / mL
Surface Group :MPA-COOH
FWHM≤ 28 nm
CdSe/ZnS QD
Grade: PL emission :545±10 nm
Concentration: 20 nmole QD / mL
Surface Group :MPA-COOH
FWHM≤ 28 nm
CdSe/ZnS QD
Grade: PL emission :525±10 nm
Concentration: 20 nmole QD / mL
Surface Group :MPA-COOH
FWHM≤ 25 nm
CdSe/ZnS QD
Grade: PL emission :470±10 nm
Concentration: 20 nmole QD / mL
Surface Group :MPA-COOH
FWHM≤ 25 nm
CdSe/ZnS QD
Grade: PL emission :450±10 nm
Concentration: 20 nmole QD / mL
Surface Group :MPA-COOH
FWHM≤ 25 nm
CdSe/ZnS QD
Grade: PL emission :645±10 nm
Concentration:10 nmole QD / mL
Surface Group :PEG-COOH
FWHM≤ 30 nm
CdSe/ZnS QD
Grade: PL emission :625±10 nm
Concentration:10 nmole QD / mL
Surface Group :PEG-COOH
FWHM ≤ 28 nm
CdSe/ZnS QD
Grade: PL emission :545±10 nm
Concentration:10 nmole QD / mL
Surface Group :PEG-COOH
FWHM≤ 28 nm
CdSe/ZnS QD
Grade: PL emission :525±10 nm
Concentration:10 nmole QD / mL
Surface Group :PEG-COOH
FWHM≤ 25 nm
CdSe/ZnS QD
Grade: PL emission :470±10 nm
Concentration:10 nmole QD / mL
Surface Group :PEG-COOH
FWHM≤ 25 nm
CdSe/ZnS QD
Grade: PL emission :450±10 nm
Concentration:10 nmole QD / mL
Surface Group :PEG-COOH
FWHM ≤ 25 nm
CdSe/ZnS QD
Grade: PL emission :645±10 nm
Concentration:25 mg QD / mL
FWHM≤ 30 nm
Quantum Yield> 85%
CdSe/ZnS QD
Grade: PL emission :625±10 nm
Concentration:25 mg QD / mL
FWHM≤ 28 nm
Quantum Yield> 85%
CdSe/ZnS QD
Grade: PL emission :545±10 nm
Concentration:25 mg QD / mL
FWHM≤ 28 nm
Quantum Yield> 85%
CdSe/ZnS QD
Grade: PL emission :525±10 nm
Concentration:25 mg QD / mL
FWHM≤ 25 nm
Quantum Yield> 85%
CdSe/ZnS QD
Grade: PL emission :470±10 nm
Concentration:25 mg QD / mL
FWHM≤ 25 nm
Quantum Yield> 85%
CdSe/ZnS QD
Grade: PL emission :450±10 nm
Concentration:25 mg QD / mL
FWHM≤ 25 nm
Quantum Yield> 85%
InP/ZnS QD
Grade: PL emission :645±10 nm
Concentration:20 nmole QD / mL
Surface Group :MPA-COOH
FWHM< 55 nm
InP/ZnS QD
Grade: PL emission :625±10 nm
Concentration:20 nmole QD / mL
Surface Group :MPA-COOH
FWHM< 55 nm
InP/ZnS QD
Grade: PL emission :565±10 nm
Concentration:20 nmole QD / mL
Surface Group :MPA-COOH
FWHM< 42 nm
InP/ZnS QD
Grade: PL emission :545±10 nm
Concentration:20 nmole QD / mL
Surface Group :MPA-COOH
FWHM< 42 nm
InP/ZnS QD
Grade: PL emission :525±10 nm
Concentration:20 nmole QD / mL
Surface Group :MPA-COOH
FWHM< 42 nm
InP/ZnS QD
Grade: PL emission :645±10 nm
Concentration:10 nmole QD / mL
Surface Group : PEG-COOH
FWHM< 55 nm